Thin film filter having negative temperature drift coefficient

ABSTRACT

A structure of a film filter includes a plurality of film layers made of a film stack material and a substrate wafer which said film layers are deposited on at a temperature substantially higher than a room temperature and retained to after being cooled to the room temperature. The substrate wafer has a coefficient of thermal expansion greater than that of the film stack material so as to generate compressive forces upon the associated film layers, thus resulting in the film filter having a negative temperature drift coefficient.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application is a divisional application of U.S. application Ser. No. 10/044,271, filed Jan. 10, 2002.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to thin film filters, and particularly to thin film filters having a negative temperature drift coefficient which can achieve better control of optical performance of an associated DWDM (dense wavelength division multiplexing) system when working within an operational temperature range.

2. Description of Related Art

In recent years, thin film filters have often been used in optical systems for signal processing or optical communications. The filters operate to select light of desired wavelengths, often within a narrow band. Thin film filters may be used in association with gradient refractive index (GRIN) lenses and optical fibers to form a dense wavelength division multiplexing (DWDM) device. Referring to FIG. 5, the operating principle of an eight-channel, filter type DWDM device is illustrated. Ideally, a light beam of a particular wavelength is considered one channel. In practice, one channel is defined by a very narrow range of wavelengths. The more channels a DWDM device has, the narrower the pass bandwidth of each channel.

To obtain narrower pass bandwidths, more layers of film are normally deposited on a glass substrate, creating a stack of films on the substrate. However, this procedure inevitably induces more internal stress in the film stack. The more tensile stress endured by a film stack, the looser the atomic structure of the films in the stack. Interfaces between film layers in the stack act as mirrors, which act to separate the wavelengths of a light beam. A looser atomic structure in a film stack lowers the reflectivity of these interfaces. Thus tensile stress in a film stack acts to broaden the pass bandwidth. Conversely, the more compressive stress endured by a film stack, the narrower the pass bandwidth of the filter is.

The coating process is designed to minimize pass bandwidth drift at room temperature (23° C.). The operational temperature range of a thin film filter is from −5° C. to 70° C. Within this temperature range, the stress in the filter varies substantially linearly with the temperature. FIG. 2 shows pass bandwidth of a conventional filter at room temperature. By way of example, Alcatel's 1915 LMI 10 mw WDM thin film filter has a positive temperature drift coefficient, 1 pm/° C. FIG. 3 shows how the pass bandwidth of Alcatel's 1915 LMI changes with a change in temperature. When the 1915 LMI's temperature increases from 23° C. to 70° C., a 47 pm pass bandwidth enlargement occurs, and when the temperature decreases from 23° C. to −5° C., a 28 pm pass bandwidth reduction occurs, as is illustrated in FIG. 3. Obviously, since temperature fluctuation and resulting pass bandwidth drift are inevitable, it is preferable if pass bandwidth is reduced more often than it is increased as the environmental temperature changes. Consequently, referring to FIG. 4, there is a demand for thin film filters having a negative temperature drift coefficient, in which pass bandwidth broadens when temperature decreases and narrows when temperature increases, as shown in FIG. 4. Note that in FIG. 4, the pass bandwidth increases less at the most extreme temperatures than for the Alcatel 1915 LMI case shown in FIG. 3.

Operational temperature fluctuation affects the stress present in a thin film filter, since film stacks and substrates of thin film filters are composed of different materials having different coefficients of thermal expansion (CTE). Thin film stacks are deposited on substrates under temperatures substantially higher than room temperature, and then are allowed to cool down to room temperature. If the CTE of a film stack is smaller than that of a substrate on which it is mounted, then the film stack will shrink less than the substrate does as they cool down. Therefore, a convex deformation occurs and a compressive stress is induced in the film stack (see FIG. 1 b). This is the case of a stack-substrate combination having a negative temperature drift coefficient.

In nearly all of the prior art, DWDM thin film filters have positive temperature drift coefficients. This is the situation illustrated in FIG. 1 a. Because the thin film stack is deposited under a temperature substantially higher than room temperature, when cooling down to room temperature, the film stack, which has a CTE greater than that of the substrate on which the film stack is mounted, shrinks more than the substrate does. Therefore, a concave deformation occurs. The film stack in this situation is under a tensile stress and pass bandwidth increases as temperature increases, which causes greater susceptibility to crosstalk as temperature increases. The tensile stress endured by the film stack is also a disadvantage during cutting operations, since it makes the affected film layers more brittle, increasing the probability of damage to the film stack during cutting. Furthermore, the adhesion between the film stack and the substrate may be overstressed, resulting in peeling of the film stack from the substrate.

SUMMARY

An object of the present invention is to provide thin film filters having a negative temperature drift coefficient, thus promoting a narrowing of pass bandwidth as temperature rises within its operational temperature range.

A structure of a film filter includes a plurality of film layers made of a film stack material and a substrate wafer which said film layers are deposited on at a temperature substantially higher than a room temperature and retained to after being cooled to the room temperature. The substrate wafer has a coefficient of thermal expansion greater than that of the film stack material so as to generate compressive forces upon the associated film layers, thus resulting in the film filter having a negative temperature drift coefficient.

There are two embodiments provided for making thin film filters having a negative temperature drift coefficient. The first embodiment comprises the steps of: (1) providing a substrate wafer which has a coefficient of thermal expansion (CTE) greater than that of a selected film stack material; (2) polishing the substrate wafer; (3) depositing thin film layers made of the film stack material on the substrate wafer at a temperature substantially higher than room temperature; (4) cooling the substrate-film stack laminate to room temperature, thus forming a convex-shaped laminate; and (5) cutting the cooled laminate into pieces at room temperature. The second embodiment comprises the steps of: (1) providing a laminate composed of a glass substrate and a film stack; (2) using at least one ion beam source to bombard the film stack of the laminate with high energy ions; and (3) cutting the bombarded laminate into pieces.

Other advantages and novel features will become more apparent from the following detailed description when taken in conjunction with the accompanying drawings, in which:

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a cross-sectional view of a thin film filter having a positive temperature drift coefficient of the prior art;

FIG. 1B is a cross-sectional view of a thin film filter having a negative temperature drift coefficient according to the present invention;

FIG. 2 is a graph of a prior art thin film filter's spectral transmittance versus wavelength characteristics, showing a pass bandwidth of the thin film filter at room temperature (23° C.);

FIG. 3 is a graph of a prior art thin film filter's spectral transmittance versus wavelength characteristics, for the case of a thin film filter having a positive temperature drift coefficient, showing a change in pass bandwidth over an operational temperature range (−5° C. to 70° C.);

FIG. 4 is a graph of a prior art thin film filter's spectral transmittance versus wavelength characteristics, for the case of a thin film filter having a negative temperature drift coefficient, showing a change in pass bandwidth over an operational temperature range (−5° C. to 70° C.); and

FIG. 5 is a schematic diagram showing the functioning of a prior art eight-channel, filter-type DWDM device.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

Two embodiments for making thin film filters having a negative temperature drift coefficient are provided.

A first preferred embodiment generally comprises five steps as follows: (1) providing a substrate wafer which has a coefficient of thermal expansion (CTE) greater than that of selected film stack material; (2) polishing the substrate wafer; (3) depositing a stack of films each having a CTE smaller than that of the substrate wafer onto the substrate at a temperature substantially higher than room temperature; (4) cooling the resulting substrate-film laminate to room temperature, thus forming a convex-shaped substrate-film laminate; and (5) cutting the cooled substrate-film laminate into pieces.

In the first step, a substrate wafer that has a CTE ranging from 10×10⁻⁶/° K. to 20×10⁻⁶/° K. is provided. The substrate wafer must be transparent in the telecommunication range, i.e., C band (1528 nm to 1561 nm) and L band (1561 nm to 1620 nm). The substrate wafer can be made of glass of a SiO₂—Na₂O—K₂O—Li₂O—PbO—XO₂ system, wherein X can be titanium (Ti) or zirconium (Zr). It can also be made of a SiO₂—Na₂O—K₂O—Li₂O—PbO-Q₂O₃ system, wherein Q can be aluminum (Al), or of a SiO₂—Na₂O—K₂O—Li₂O—P₂O₅-ZO₂ system, wherein Z can be titanium (Ti) or zirconium (Zr). To increase the CTE of the glass substrate to the desired range, the substrate wafer can be doped with lead (Pb), lithium (Li), sodium (Na), potassium (K), or some other alkali ions or oxides.

In order to increase the adhesion between the film stack and the substrate wafer, in the second step, the substrate wafer is polished to a roughness in the range of from 0.1 nm to 0.8 nm.

Then, in the third step, Ta₂O₅/SiO₂,which has a CTE ranging from 1×10⁻⁶/° K. to 8×10⁻⁶/° K., is used as a material for the thin film stack deposited on the substrate. Each film layer is made of the film stack material, and a chemical vapor deposition (CVD) method is preferred for depositing the film layers on the substrate and on each other. In this step, the substrate and film layers are substantially planar during the layering process. The process is conducted at a temperature substantially higher than room temperature.

In the fourth step, the substrate and film layers laminate produced in step three is cooled down. Referring to FIG. 1 b, since the CTE of the substrate wafer is greater than that of the film layers, when cooling down in the fourth step, the substrate wafer shrinks more than the film layers do. Therefore, the resulting laminated substrate and film layers will become slightly convex, and the film layers will endure a compressive stress at room temperature.

Finally, in the fifth step, the convexly shaped laminate of the substrate and film layers is cut into pieces, each having a negative temperature drift coefficient and compressive stress distribution in its film stack at room temperature.

A second preferred embodiment comprises three steps as follows: (1) providing a laminate comprising a glass substrate and a film stack; (2) providing at least one ion beam source for use in bombarding the film stack in the laminate; and (3) cutting the bombarded laminate into pieces.

In the first step of the second embodiment, a laminate made of a glass substrate and thin film stack is put in a target position. In the second step, at least one ion source is heated to release ions. The ions are then accelerated by an electric field to bombard the film stack in the target laminate. Before reaching the target, the mean energy of the ions is between 100 and 1500 electron-volts. The ion beam source may be a Kaufman source. The bombarding ion beam causes the structure of the film stack to condense. A denser structure means closer distances between adjacent atoms in the film stack, which induces a compressive stress in the film stack. Finally, in the third step, the resultant bombarded laminate is cut into pieces to obtain the DWDM filter devices with a desired negative temperature drift coefficient.

The method described in the first preferred embodiment can be used with the second. Thin film filters made using the above described methods have a more dependable optical performance in a DWDM system when working within their operational temperature range. It is to be understood that the above-described preferred embodiments are intended to exemplify the invention without limiting its scope. In addition, even though numerous characteristics and advantages have been set forth in the foregoing description, together with details of the structures and functions of the thin film filters, the disclosure is illustrative only. Changes may be made in detail, especially in matters of obviously similar materials, processes and equipment, within the principles of the present invention to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed. 

1. A structure of a film filter comprising a plurality of film layers made of a film stack material and a substrate wafer which said film layers are deposited on at a temperature substantially higher than a room temperature and are retained to after being cooled to the room temperature, wherein said substrate wafer has a coefficient of thermal expansion greater than that of the film stack material so as to generate compressive forces upon the associated film layers, thus resulting in a negative temperature drift coefficient of said film filter.
 2. The structure of the film filter as described in claim 1, wherein the coefficient of thermal expansion of the substrate is in the range from 10×10⁻⁶/° K. to 20×10⁻⁶/° K.
 3. The structure of the film filter as described in claim 1, wherein the substrate wafer is transparent to electromagnetic waves having a wavelength in the range from 1561 nm to 1620 nm.
 4. The structure of the film filter as described in claim 1, wherein the substrate is made of a SiO₂—Na₂O—K₂O—Li₂O—PbO—XO₂ system, wherein X is titanium (Ti) or zirconium (Zr).
 5. The structure of the film filter as described in claim 1, wherein the substrate is made of a SiO₂—Na₂O—K₂O—Li₂O—PbO—Al₂O₃ system.
 6. The structure of the film filter as described in claim 1, wherein the substrate is made of a SiO₂—Na₂O—K₂O—Li₂O—P₂O₅-ZO₂ system, wherein Z is titanium (Ti) or zirconium (Zr).
 7. The structure of the film filter as described in claim 1, wherein the substrate wafer is doped with at least one of a group comprising lead (Pb), lithium (Li), sodium (Na), and potassium (K).
 8. The structure of the film filter as described in claim 1, wherein a deposition surface of the substrate wafer has an average roughness in the range of from 0.1 nm to 0.8 nm.
 9. The structure of the film filter as described in claim 1, wherein the film stack material comprises tantalum oxide and silicon dioxide.
 10. The structure of the film filter as described in claim 1, wherein the film stack endures a substantially compressive stress at room temperature.
 11. A structure of a film filter comprising a plurality of film layers made of a film stack material and a substrate wafer which said film layers are deposited on and retained to, wherein said substrate wafer has a coefficient of thermal expansion greater than that of the film stack material, and from a microscopic viewpoint both said substrate wafer and said film layers commonly define a convex configuration under a condition that said substrate wafer is located closer to a center of said convex configuration than said filter layers.
 12. A structure of a film filter comprising a plurality of film layers made of a film stack material and a substrate wafer which said film layers are deposited on and retained to, said substrate wafer having a coefficient of thermal expansion greater than that of the film stack material whereby said film filter has a negative temperature drift coefficient in comparison with a positive temperature drift coefficient of a conventional film filter, said film filter being characterized in that: within a range between a higher temperature and a lower temperature including a room temperature, the range corresponding to a normal bandwidth of said film filter, said film filter at said lower temperature results in a broadened bandwidth with an increased value smaller than another increased value of another broadened bandwidth resulting from said conventional film filter at said higher temperature, and said film filter at said higher temperature results in a narrowed bandwidth with a reduced value smaller than another reduced value of another narrowed bandwidth resulting from said conventional film filter at said lower temperature. 